Carbon Fiber Precursor Production Line
Nkọwa
Usoro mmepụta carbon fiber precursor nke na-anabata Dimethyl Sulfoxide (DMSO) dị ka ihe mgbaze, Acrylonitrile (AN) dị ka monomer nke mbụ, Itaconic Acid dị ka monomer nke abụọ, AIBN dị ka onye mbido inwe ọnụọgụ abụọ copolymerization, na mmiri mmiri na-agba mmiri. bụ nhọrọ kacha elu kwetara n'etiti ndị ọkachamara fiber carbon.
Ụdị teknụzụ:
| Mba. | Ihe | Nkeji | Nkọwapụta | Okwu |
| 1 | Njupụta Linear | dtex | 1.15 | |
| 2 | Ike ọdụdọ | CN/dtex | ≥4.0 | |
| 3 | Ogologo oge | % | 12±2 | |
| 4 | Ọdịnaya Dimethyl Sulfoxide (DMSO). | % | 00.03 | |
| 5 | Ọdịnaya mmanụ | % | 0.5-0.1 | |
| 6 | Ọnụego nkwụsịtụ | % | 3 | |
| 7 | Weghachite mmiri | % | ≤1 | |
| 8 | Ọdịdị | Ọnweghị eriri agbajiri pụtara |
Usoro:
Nkwadebe ihe eji eme ihe -→ Ngwakọta monomer - → copolymerization —→ Isi nzacha — → Monomer Nwepu —→ Secondary filtration —→ Mixed Batch Neutralization —→ Tertiary filtration —→ Nchekwa — → Defoam — → Spinning — → spin bath (Primary) —→ atụ ogho bath (Secondary) - → spin bath (Tertiary) -→ Dị ọcha -→ Mgbatị ọkụ - → mmanu - ihicha - → Mgbatị uzuoku -→ Ntọala okpomọkụ -→ Ọgwụgwọ Antistatic - → Precursor Winding
| Mba. | Ihe | Nkeji | Nkọwapụta | Okwu |
| 1 | Njupụta Linear | dtex | 1.15 | |
| 2 | Ike ọdụdọ | CN/dtex | ≥4.0 | |
| 3 | Ogologo oge | % | 12±2 | |
| 4 | Ọdịnaya Dimethyl Sulfoxide (DMSO). | % | .0.03 | |
| 5 | Ọdịnaya mmanụ | % | 0.5-0.1 | |
| 6 | Ọnụego nkwụsịtụ | % | .3 | |
| 7 | Weghachite mmiri | % | ≤1 | |
| 8 | Ọdịdị | Ọnweghị eriri agbajiri pụtara |
Raw Nkwadebe ihe - → Ngwakọta monomer — → Copolymerization —→ Primary filtration —→ Monomer Removal —→ Secondary filtration —→ Mixed Batch Neutralization —→ Tertiary filtration —→ Nchekwa — → Defoam — → Spinning — → spin bath (Primary) — → atụ ogho bath (Secondary) - → spin bath (Tertiary) -→ Dị ọcha -→ Mgbatị ọkụ - → mmanu - ihicha - → Mgbatị uzuoku -→ Ntọala okpomọkụ -→ Ọgwụgwọ Antistatic - → Precursor Winding